TOTAL PRO GF 10 1,75mm 750 gr

52,00

Impact-resistant glass-filled (10%) composite based on TPU with heat resistance up to 110oC for printing large gears, strong housings, mechanically loaded parts, aerodynamic body kits for cars.
It has a high chemical resistance to acid and alkali solutions, fats, oils, xylene, diesel fuel. Limited to gasoline, kerosene, acetone, dichloromethane.

To avoid leaking plastic from the nozzle, dry it before printing and maximize the speed of the idle movement of the extruder (travel speed).

Clear
SKU: 369918465081 Category:

Description

TOTAL PRO GF 10 impact-resistant glass-filled (10%) composite based on TPU GF 10 with heat resistance up to 110°C for printing large gears, strong housings, mechanically loaded parts, aerodynamic body kits for cars.
It has a high chemical resistance to acid and alkali solutions, fats, oils, xylene, diesel fuel. Limited to gasoline, kerosene, acetone, dichloromethane.
Thanks to its low shrinkage (up to 0.9%), good interlayer adhesion and high abrasion resistance, TOTAL GF 10 plastic will be an excellent alternative to polyamide-based composites.
Perfectly amenable to drilling, threading.

For best results, it is recommended to dry before printing for 2-3 hours at a temperature of 65-75°C.

ATTENTION! Plastic is abrasive, it is recommended to print using a steel nozzle.

We can print your 3D model with TOTAL PRO GF 10

Print Options
Nozzle temperature                             220-245°C
Printing table temperature                   60-100°C
Blowing the model as needed             20-60%
Print speed up to                                100 mm / s
Plastic feed (Flow)                              95-100%
Nozzle diameter from                         0.4 mm (min)
Min. layer height                                 0.1 mm
Heat resistance (min / max)               -50 to +110°C
Rod diameter tolerance                      0.03 mm
Quantity per coil                                 ~215m
Shore hardness                                   D 85
Elongation at break                              15%
Tensile modulus of elasticity             3000 Mpa
Maximum tensile strength                   ~75 Mpa
VIC softening point                             110°C
Density                                             ~1.4 g / cm3
Charpy impact strength                   (+23 C) 140 kj / m2
Charpy impact strength                   (-30 C) 80 kj / m2
Notched Sharpie impact strength    (+23 C) 35 kj / m2
Notched Sharpie impact strength    (-30 C) 10 kj / m2
Shrinkage in the manufacture of products     0.3-0.9%

Additional information

Weight 1 kg
Dimensions 21 × 21 × 7 cm
Colour

Black, White